Carbon fibre prepregs

Prepregs are fibre reinforcements pre-impregnated with catalysed resin under pressure, temperature or using solvents with different weave patterns, fibre types etc.

The hardening agent for the resin system, a defined concentration of which is applied to the carrier material, is adjusted so that the materials can be stored for several days or months at room temperature without reaction, but they often also need to be kept cool to guarantee processing quality.

The range of uses for carbon fibre prepreg is as varied as the product itself. It can be processed using common methods or varied on a project-specific basis. Uses for our prepreg include high-quality optical applications and structural or flame-retardant composite components.

Our epoxy resin systems can be processed between 80 and 160 °C and are available with a UD carbon fibre base material of HT or HM carbon fibres or with different woven / non-crimp base materials.

The following 120° systems are usually available at short notice:

	Carbon material	Resin content [mass-%]	Width [cm]
High-modulus-UD-prepreg	UD 100g/m², Pyrofil HR40 12K	36	34
Ultra-high-modulus-UD-prepreg	UD 250g/m2, Dialead K63716	38	30
Ultra-high-modulus-UD-prepreg	UD 450g/m², Dialead K63716	36	63,5
Carbon-UD-prepreg	UD 150g/m²	39	60
Carbon-UD-prepreg	UD 200g/m²	40	63,5
Carbon-UD-prepreg	UD 230g/m²	38	56
High-modulus-UD-prepreg	UD 255g/m²	37	60
Carbon-UD-prepreg	UD 300g/m²	36	54
Carbon-UD-prepreg	UD 600g/m²	40	130
Carbon fabric prepreg	165g/m² plain	42	120
Carbon fabric prepreg	3K fabric twill 2/2 200g/m²	42	125
Carbon fabric prepreg	3K fabric twill 2/2 245g/m² DESIGN	43	100
Carbon fabric prepreg	3K fabric twill 4/4 285g/m²	47	125
Carbon fabric prepreg	12K fabric twill 2/2 420g/m²	42	100
Carbon fabric prepreg	12K fabric twill 2/2 600g/m²	38	125
Carbon non-crimp prepreg +/-45°	400 g/m², +/-45°	40	127

further items available on request

Most carbon fibre fabrics and biaxial non-crimp fabrics are also available as prepreg.