CF-Epoxy boards

Dependent upon the specific technical requirements, both the type of fibre and its orientation as well as the matrix system can be modified. The surfaces can be supplied with a coarse, matt, grinded, textured or high gloss finish, according to the customer’s wishes.

  • high gloss finish on both sides from 0,5 mm thickness

  • one side high gloss finish, one side coarse finish (protected by peel ply) from 0,3 mm thickness

  • coarse finish on both sides (protected by peel ply) from 0,3 mm thickness

  • grinded surface from 1 mm thickness

  • fibre orientation freely selectable (unidirectional, bi-axial, multi-axional)

  • also available made of high-modulus fibre

    • Carbon fibre CFRP semi-finished plates

      Carbon high gloss finish

    • Carbon fibre reinforced semi-finished boards, Carbon epoxy plates,

      Carbon textured finish

    • Carbon composite, carbon sheets thermoset CF/epoxy

      Carbon matt finish

    • CF Epoxy  CFRP CF/epoxy laminates , carbon fiber reinforced boards with epoxy matrix waterjet cutted

      CF-epoxy waterjet-cutted

characteristic values CF-epoxy boards

The data sheet shows only examples of our CF-epoxy board spectrum. Further matrix systems (both thermoset and thermoplastic), type of fibres or additional dimensions may be available on request.

fibre orientation

0/90°

0/-45/+45/90°

standard dimension [mm]

1220x970

1220x970

1220x480

thickness [mm]

0,5-100

6-200

3-50

fibre

HT-Carbon

HT-Carbon

UHM-Carbon

fibre volumecontent [%]

ca. 55

ca. 55

ca. 60

density (g/cm³)

1,5

1,5

1,7

tensile strength 0° Mpa

550

320

1300

tensile strength 90° Mpa

550

320

35

tensile strength +/- 45° Mpa

120

320

50

elastic modulus 0° Gpa

60

35

370

elastic modulus 90° Gpa

60

35

5

elastic modulus +/- 45° Gpa

15

35

10

max. service temperature [°C]

100

125

110

The information in our technical documents is reliable and related to practice, however it remains the customers responsibility to examine our products in regard to the intended purpose and process.